Magnesium Aluminium Bricks

  • Magnesium Aluminium Bricks


1.High softening temperature

2.Good thermal shock resistance

3.High mechanical strength at high temperature 
Magnesium Aluminium Bricks Introduction
 
Magnesia aluminum bricks use magnesia as the main raw material, magnesia brick and aluminum oxide as the co-milled fine powder as the matrix, the alkaline products which are fired at high temperature are called magnesia alumina bricks.
 
Magnesia aluminum refractory bricks have good thermal shock resistance, high mechanical strength at high temperatures and high softening temperatures.
 
Magnesium aluminum fire brick has good slag resistance, high temperature performance and thermal stability, and the price is cheaper than magnesium spinel.
 
Magnesium Aluminium Bricks Features
 
*Magnesium-aluminum bricks has good slag resistance

*Magnesium-aluminum bricks has good thermal shock resistance

*Magnesium-aluminum bricks has high load softening temperature

*Magnesium-aluminum bricks has high temperature mechanical strength

*Magnesium-aluminum bricks has high temperature performance & thermal stability
 
Magnesium Aluminium Bricks Specification
 
Index
Item
  RS-A RS-80 RS-85 RS-88
MgO % 86 85 88 90
Al2O3 % 5 7 6.5 6.5
SiO2 % 3.2 4 2.4 1.2
CaO % 1.6 1.5 1.3 1.2
Fe2O3 % 3.7 1.7 1.4 1.0
Apparent Porosity % 16~20 17 17 17
Density Bulk g/cm3 2.85~3.0 2.93 2.93 2.94
Cold Crushing Strength Mpa 41 50 50 55
0.2Mpa Under Load Refractoriness ≥ 1550 1610 1650 1700
Thermal Shock Resistance(1100℃,water,quenching, cycle)   3~6 3~6 3~6 3~6
 
Magnesium Aluminium Bricks Application
 
1.Magnesium aluminium bricks used in ladle

2.Magnesium aluminium bricks used in mixed iron furnace  

3.Magnesium aluminium bricks used in glass kiln regenerator

4.Magnesium aluminium bricks used in steel reverberative kiln roof

5.Magnesium aluminium bricks used in steel making furnace permanent lining

6.Magnesium aluminium bricks used in refractory industrial high temperature kiln
 
Magnesium Aluminium Bricks Manufacturing Process
 
1.The production process of magnesia aluminum bricks is roughly the same as that of calcined magnesia bricks, except that a certain proportion of industrial alumina or extra-grade bauxite clinker is added to the ingredients.
 
2.Industrial alumina has a lower impurity content than high alumina bauxite. The addition of natural bauxite clinker to the ingredients can improve the plasticity of the mud. Under the same conditions, the bulk density of the magnesia alumina bricks is higher. Industrial alumina is generally added in an amount of 5% to 10%, refractory magnesia alumina is usually finely ground with magnesia in a certain proportion, and then added as a fine powder, which is advantageous for forming a uniform distribution of the magnesium-aluminum spinel new crystal phase in the matrix of the product.
 
3.There are also production methods using pre-synthesized magnesium aluminum spinel refractory bricks for batching bricks. The critical particle size during the batching is beneficial to improve the thermal shock resistance of the product, but magnesium alumina bricks are not conducive to the density and strength of the product, and generally adopts 3 mm.
 
4.The particle size is generally 3 to 1 mm and 1 to 0.088 mm the ratio of 3 to 2 mm coarse particles to less than 0.088 mm fine powder should be controlled to improve the thermal shock resistance of the product. The firing temperature of the magnesium aluminum fire brick is determined according to the purity of the raw material, generally 30 to 50 ° C higher than the firing temperature of the magnesium brick, and the firing temperature of the high purity magnesium aluminum brick is 1750 to 1800 ° C.
 
Magnesium Aluminum Bricks Compared with Magnesia Bricks Advantages
 
1.Magnesium aluminum brick has good thermal shock resistance and can withstand water cooling for 20 to 25 times or even higher. This is its most prominent advantage, much better than ordinary magnesia bricks. The study believes that the thermal shock resistance of magnesium aluminum bricks is good because both magnesium aluminum spinel bricks and periclase belong to the cubic system, the thermal expansion along the direction of each crystal axis is the same, so the expansion and contraction are more uniform when the temperature fluctuates. The resulting thermal stress is small.
 
2.The main properties of 2 magnesia aluminum refractory bricks are also slightly stronger than those of magnesia bricks. Since the melting point of the magnesium aluminate spinel bricks are higher, the load softening temperature of the magnesium aluminum brick is improved compared with the magnesium brick, reaching 1620 to 1690 °C.
 
3.The ability of magnesium aluminum spinel bricks to protect the cristobalite particles from slag erosion is stronger than that of calcium-magnesium olivine, so the ability of magnesium aluminum firebricks to resist alkaline slag and iron oxide slag is stronger than that of magnesia bricks.
 
RS Refractory Factory Provide High Quality Service
 
If you make sure what firebricks you need ,please provide the drawings you used in the past, we can do better ,satisfy your any technology requests.
 
RongSheng Refractory Factory have the professional sales team,if you have any smaller problem ,we can solve them at any time. We treat every client as a friend ,friend is precious.
 
In your inquiry ,please provide detailed information you known ,thank you.