Magnesia Chrome Bricks for Arc Furnace

  • Magnesia Chrome Bricks for Arc Furnace



1.High refractoriness.

2.High temperature strength.

3. Excellent thermal stability.

4.Strong resistance to alkaline slag.
Magnesia Chrome Bricks for Arc Furnace Introduction
 
Magnesia chrome bricks for Arc Furnace have high refractoriness, high temperature strength, strong resistance to alkaline slag, excellent thermal stability, certain adaptability to acidic slag. Magnesia chrome bricks are refractory products containing MgO and Cr2O3 as the main components, the periclase and spinel are the main mineral components. The main refractory raw materials of magnesia chrome refractory bricks are sintered magnesia and chromite. The purity of the magnesia raw material should be as high as possible.
 
Magnesia Chrome Bricks for Arc Furnace Features
 
1.Magnesia chrome bricks have high refractoriness.
 
2.Refractory magnesia chrome bricks have high temperature strength.
 
3.Magnesia chrome refractory bricks have excellent thermal stability.
 
4.Fireproof magnesia chrome refractory bricks have strong resistance to alkaline slag.
 
Magnesia Chrome Bricks for Arc Furnace Property
 
1 Chemical Composition and Mineral Composition
 
The chemical composition of magnesia chrome refractory bricks varies with the ingredients used. Generally, the total amount of magnesium oxide is 55% to 60%, the chromium oxide is about 10%, followed by impurities such as ferric oxide and a small amount of alumina, silica, and calcium oxide. The mineral composition of magnesia chrome fire bricks are mainly magnesium chrome spinel bricks and magnesium ferrite.
 
2 Magnesia Refractory Bricks Refractoriness
 
Because the content of periclase in magnesia chrome fire brick is less than that of magnesia brick, the content of magnesia chrome spinel bricks and magnesium ferrite is much, the melting point of their eutectic compound is relatively low. Therefore, the magnesia chrome refractory brick is low, generally only 1850. ~1960°C.
 
3 Magnesia Fire Bricks Have Load Softening Temperature
 
The periclase crystal and the magnesia chrome spinel refractory bricks in the magnesia chrome refractory bricks are easy to form a network skeleton, because the low melting point filled in the network gap is less quality, when subjected to high temperature load, although the low melting point material softens, the mesh is soft. The skeleton can still support the load, so the load softening temperature of the magnesia chrome refractory brick is higher, generally up to 1550 °C. The degree of refractoriness of magnesia chrome refractory brick is slightly lower than that of magnesia refractory bricks, the load softening temperature is higher than that of magnesia fire bricks.
 
4 Magnesia Chrome Bricks Have Thermal Expansion and Thermal Shock Stability
 
Among the refractory magnesia chrome bricks, the content of magnesia chromium spinel and magnesium ferrite is large and the coefficient of linear expansion is small. The content of calcium magnesium olivine in magnesia chrome brick is very small, it is not easy to cause anisotropic expansion stress; magnesium ferrite is dissolved in magnesia-chromium spinel, solubility is large, the dissolution temperature range is also wide, the dissolution and precipitation of magnesium ferrite.  It does not cause large stresses. Therefore, the thermal shock stability of magnesia chrome firebricks was good, the number of water cooling can reach about 25 times. Meanwhile, the porosity of magnesia chrome firebrick is larger than that of rmagnesia brick, so the thermal expansion property of magnesia chrome brick is small.
 
5 Magnesia Chrome Bricks Have Slag Resistance
 
Magnesia chrome spinel refractory bricks is a composite of magnesium oxide and chromium oxide, chromium oxide is a typical neutral oxide. Therefore, magnesia chrome refractory bricks attack alkaline and acid slag,and have strong resistance.
 
Magnesia Chrome Bricks for Arc Furnace Specification
 
Index
Item
RS-MGe6 RS-MGe8 RS-MGe12 RS-MGe16 RS-MGe20 RS-MGe22 RS-MGe26 RS-MGeB RS-MGeB10
Mgo(%) 80 72 70 65 56 49 45 71 67
Cr2O3(%) 7 10 13 17 22 24 27 9.6 12
CaO(%) 1.2 1.2 1.2 1.2 1.2 1.2 1.2 1.5 1.5
SiO2(%) 3.8 4 4 4.2 3 4.5 5 3.5 3.8
Al2O3(%) 4.5 6.5 6 6 10.5 11 12 6 6.5
Fe2O3(%) 4 4.8 5.5 6.5 7.3 10 10 8.5 9
Apparent porosity(%) 17 18 18 18 19 20 20 12 12
Bulk Density (g/cm3) 3 3 3.02 3.05 3.07 3.02 3.1 3.1 3.1
Cold Crushing
Strength(Mpa)
55 55 55 50 50 55 45 80 80
0.2Mpa under load
Refractoriness ( ℃)
1600 1600 1600 1600 1620 1620 1620 1570 1570
 
 
Magnesia Chrome Bricks for Arc Furnace Manufacture Process
 
1.Magnesia Chrome Bricks Particulate Component
 
The proportion of chromium ore and magnesia added is determined according to the requirements of Cr2o3 content and the actual content of CrO2 in chromium ore.
 
The choice of size is adjusted to the environment in which the magnesia chrome refractory brick is used.
 
The most common practice is to add the chrome ore as a particulate component, which is added as a fine powder and a portion of the particulate component.
 
When emphasizing the thermal shock resistance of magnesia chrome bricks, the granule limit of chrome ore is added or the proportion of chrome ore coarse particles is increased.
 
When emphasizing the corrosion resistance of magnesia chrome bricks, a fine powder of magnesium ore and a part of chrome ore is added.
 
2.Magnesia Chrome Bricks Mixing 
 
In a wet mill, a mixer, and a powerful countercurrent mixer.
 
Bonding agent: sulfite pulp waste liquid, brine, magnesium sulfate solution, can be used, and the amount added is about 3%.
 
Feeding sequence: first add particles and then add binder solution, then add fine powder, etc. When the CaO content in the brick is high, the material can be used as needed to prevent brick cracking.
 
3.Magnesia Chrome Bricks Molding
 
Magnesia chrome refractory bricks can be formed by friction brick pressing, the hydraulic pressing machine can be pressed on both sides to make the density of the blank uniform. Light and heavy first, multiple pressurization is beneficial to the exhaust, preventing the brick from cracking due to elastic after effect.
 
Magnesia Chrome Bricks Drying
 
The purpose of drying is to remove the physical water in the green body binder to increase the height of the refractory brick, reduce the bricks and burn waste, generally used tunnel kiln dryer drying.
 
Magnesia Chrome Bricks Yards Refractory Brick
 
The code bricks of magnesia chrome bricks should be left with a larger fire channel, appropriately reduce the density of the bricks, increase the heating speed of the bricks in the pre-tropical zone.
 
Magnesia Chrome Bricks Manufacturer in RS Refractory Factory
 
Rongsheng kiln refractory material factory specializing in the production of refractory bricks for nearly 20 years, now has formed a comprehensive enterprise for the production of refractory materials for the metallurgy, building materials, power, and chemical industries.
 
1.Rongsheng refractory bricks manufacturer have strong production capacity, supply is guaranteed.
 
2. Rongsheng refractory bricks company has professional refractory brick production plants and amorphous refractory production plants.
 
3.Rongsheng refractory bricks manufacture have advanced concepts and scientific management.
 
4.Rongsheng refractory bricks manufacture have perfect after-sales service system
 
From raw material procurement to final product inspection and after-sales service. Ensure that the product offered to the user is 100% qualified.